The effects of TiO2 nanotubes on bond strength and radiopacity of a self-adhesive resin cement in self-curing mode / Os efeitos de nanotubos de TiO2 na resistência de união e radiopacidade de um cimento resinoso auto-adesivo no modo auto-polimerizável

Objective: The aim of this in vitro study w as t o analyze the influence of the titanium dioxide nanotubes i n a self-cure mode polymerization of a dual resin luting agent through push out bond strength and radiopacity tests. Material and Methods: After mixed with a commercial du al self-adhesive resin cement, three concentrations o f tit anium dioxide nanotubes (0.3, 0.6, and 0.9% by weight) we re analyzed in self-curing mode. T he bond strength to bovine root dentin and fi berglass posts was assessed with the push out bond str ength t est and was evaluated in three thirds (cervical, middle and apical) (n=10), followed by failure mode analysis (SEM), and the ISO standard 9917-2 was followed for radiopacity test (n=10). Data were statistically analyzed by one-way ANOVA test, followed by Tukey's test (α=0.05). Results: Reinforced self-adhesive resin cement with 0.6% titanium dioxide nanotubes showed significant difference compared to the control gr oup for push out test (p=0.00158). The modified groups did not s how significant difference among thirds (p=0.782). Radiopacity sh owed higher value for group w ith 0.9% titanium dioxide nanotubes in comparison w ith control group (p<0.001). Conclusion: The addition of titanium dioxide nanotubes to a self-adhesive resin cement increased the bond strength to dentin and radiopacity values in the self-cure polymerization mode (AU)

Objetivo: O objetivo deste estudo in vitro foi analisar a influência de nanotubos de dióxido de titânio na polimerização química de um agente cimentante resinoso dual através de testes de resistência à união e radiopacidade. Material e Métodos: Após misturado com um cimento resinoso auto-adesivo comercial, três concentrações de nanotubos de dióxido de titânio (0,3, 0,6 e 0,9% em peso) foram analisadas. A resistência da união para a dentina da raiz bovina e os pinos de fibra de vidro foi avaliada pelo teste de push-out e avaliada em três terços (cervical, médio e apical) (n = 10), seguido pelo análise de modo de falha (MEV) e a norma ISO 9917-2 foi seguido para teste de radiopacidade (n = 10). Os dados foram analisados estatisticamente pelo teste ANOVA um fator seguido do teste de Tukey (α = 0,05). Resultados: O cimento resinoso auto-adesivo reforçado com nanotubos de dióxido de titânio a 0,6% mostrou diferença significativa em comparação com o grupo controle para teste de push-out (p=0,00158). Os grupos modificados não mostraram diferença significativa entre os terços (p=0,782). A radiopacidade mostrou maior valor para o grupo com nanotubos de dióxido de titânio 0,9% em comparação com o grupo controle (p<0,001). Conclusão: A adição de nanotubos de dióxido de titânio a um cimento resinoso auto-adesivo aumentou a os valores de resistência de união à dentina e radiopacidade no modo de polimerização química do agente cimentante (AU)

Utilidad de la radiografía de abdomen en el diagnóstico de la intoxicación medicamentosa: reporte de un caso pediátrico / Use of abdominal X-ray in drug intoxication: a pediatric case report

Las intoxicaciones medicamentosas son un motivo de consulta frecuente en pediatría, además de una de las principales causas externas de mortalidad en adolescentes. El diagnóstico y tratamiento tempranos son fundamentales para el manejo adecuado de estos casos. Se presenta una niña de 13 años que, luego de ingerir un fármaco desconocido, muestra decaimiento y manifestaciones clínicas gastrointestinales. Por sospecha de intoxicación con hierro y la imposibilidad de determinar los niveles de sideremia de manera urgente, se realiza radiografía de abdomen, que confirma el diagnóstico y permite el tratamiento adecuado de la paciente. En este caso, se destaca la utilidad de la radiología para el diagnóstico en la sospecha de intoxicación con hierro, gracias a la radiopacidad de sus sales

Drug intoxication is a common reason for pediatric emergency department (ED) visits and one of the leading causes of death among teenagers. Early diagnosis and treatment are essential for a proper management of these patients. We present a 13-year-old girl attended at the ED showing excessive sleepiness and gastrointestinal symptoms after taking an unknown drug. Due to suspected iron overdose and the impossibility of measuring urgent iron levels, an abdominal X-ray was performed, which confirmed the diagnosis. We highlight the utility of radiology in the diagnosis of iron poisoning, which is possible due to its radiopacity.

A comparison of the physicochemical properties of AH Plus Jet with samples taken from the beginning, middle and final portions of the automix syringe system

Aim To evaluate physicochemical properties and semi-quantitative elemental analysis of AH Plus Jet with samples from the beginning, middle and final portions of the automix syringe system. Methodology Three experimental groups based on the source of the material used (beginning, middle and final portion) were established for each of the evaluated properties. Setting time, flow and radiopacity were evaluate following ANSI/ADA n. 57 specification. Set specimens was used in the semi-quantitative elemental analysis in an energy-dispersive X ray spectroscopy and scanning-electron microscopy (EDS/SEM). Statistical analysis was performed using one-way ANOVA followed by Tukey test (P<0.05). Results Flow, setting time, solubility and EDS/SEM tests showed no significant differences among the three portions of the automix syringe (P>0.05). Radiopacity test showed significant differences in the beginning of the syringe comparing to the middle and final portions (P<0.05). EDS/SEM analysis identified the presence of C, O, Al, Ca, Zr and W. The element Al, however, was found only in the final portion of the syringe. Conclusions The results of AH Plus Jet suggested an adequate ratio of the components, without segregation between organic and inorganic components, since the results of setting time, flow, solubility and EDS/SEM analysis presented similar values regardless of the portion of the syringe from where the sealer was taken.

The effect of adding ytterbium trifluoride on the radiopacity, compressive strength, setting time and bioactivity of biodentine: an in vitro study / Efeito da adição de trifluoreto de itérbio na radiopacidade, resistência à compressão, tempo de presa e bioatividade da biodentina: estudo in vitro

Objective: This study aimed to evaluate the radiopacity, compressive strength, setting time and bioactivity of Biodentine after modification with Ytterbium Tri-Fluoride (YbF3) in three different concentrations. Material and Methods: Radiopacity was determined using the equivalence in millimeters of aluminum (mm Al) from digital radiographs. Compressive strength was evaluated using a universal testing machine. The initial and final setting times were evaluated using Gillmore needle. The bioactive potential was evaluated using the environmental scanning electron microscope (ESEM) connected with Energy Dispersive X-ray analysis (EDX) and X-ray Diffractometer (XRD) at three different time intervals. pH was measured using a pH-meter. Data were analyzed using one-way ANOVA followed by Tukey's post hoc tests (P≤ 0.05). Results: Radiopacity of Biodentine with 2.5%, 5% and 7.5% YbF3 was significantly higher than unmodified Biodentine (P ≤ 0.05). Unmodified Biodentine showed the highest mean compressive strength values compared to all other groups (p≤ 0.05). The addition of YbF3 to Biodentine has extended the final setting time except for the 2.5% YbF3 group that showed no significant difference compared to the control. All groups showed an alkaline pH at 28 days, ESEM coupled with EDX analysis showed evidence of dense globules of calcium phosphate on the surface indicating enhancement of bioactivity. Conclusion: 2.5% YbF3 can be a promising radiopacifying agent to Biodentine with improvement in radiopacity, bioactive potential and maintaining the setting time and compressive strength at acceptable level as indicated by the ISO standards (AU)

Objetivo: O estudo buscou avaliar a radiopacidade, resistência à compressão, tempo de presa e bioatividade da Biodentina modificada por Trifluoreto de itérbio (YbF3). Materiais e Métodos: YbF3 foi incorporado ao pó de Biodentina e dividido em 4 grupos (X0, X1, X2 e X3) de acordo com a concentração de YbF3; 0%, 2.5%, 5% e 7.5% do peso, respectivamente. Os espécimes foram preparados para cada experimento com um total de 40 espécimes para cada teste (n=10 por grupo). A radiopacidade foi determinada através do uso equivalente em milímetros de alumínio. A resistência a compressão foi avaliada através do uso de uma máquina de teste universal. O tempo inicial e final foi avaliado através de uma agulha de Gillmore. O potencial bioativo foi avaliado através do Microscópio Eletrônico de Varredura (ESEM), conectado com a análise de espectroscopia de raios X por energia dispersiva (EDX) e difração de raio X (DRX). O pH foi mensurado através do uso de um pHmetro. Os dados foram analisados pelo ANOVA seguido do Test Tukey. Resultados: A radiopacidade nos grupos X1, X2 e X3 foi significantemente maior do que no grupo X0. O grupo X0 mostrou a maior resistência à compressão comparado com os outros grupos. A adição de YbF3 a Biodentina excedeu o tempo final exceto pelo grupo X1, que não apresentou diferença estatística significante quando comparado com o grupo X0. Todos os grupos apresentaram um pH alcalino com 28 dias. ESEM com análise EDX mostrou evidência de densos glóbulos de fosfato de cálcio na superfície, indicando uma melhora na bioatividade. Conclusão: 2.5% YbF3 é um promissor radiopacificador para Biodentina, que aumentou a radiopacidade e potencial bioativo enquanto manteve o tempo definido e a resistência à compressão em níveis aceitáveis como indica a norma ISO.(AU)

Energy-Dispersive X-Ray Spectrometry Analysis and Radiopacity of Five Different Root Canal Sealers

Abstract Root canal sealers should have optimum adhesion to the root dentin, low cytotoxicity, sufficient radiopacity and high dimensional stability, which depend mainly on their chemical composition. The aims of this study were to evaluate the chemical composition of Syntex (Cerkamed, Stalowa Wola, Poland), Adseal (Meta Biomed, Cheongju-si, Korea), Sealapex (SybronEndo, Scafati, Italy), MTA Fillapex (Angelus, Londrina, Brazil) and GuttaFlow Bioseal (Coltene/Whaledent, Altstätten, Switzerland) and to determine their radiopacity comparatively. Stainless steel molds with an inner diameter of 5 mm and a depth of 2 mm were constructed. Tested root-canal sealers were mixed and poured into the molds. Following setting, digital periapical radiographs of the specimens (n=12) were taken under standard exposure conditions and the mean gray-values of specimens were measured using a computer graphics program. Then the specimens were examined by scanning electron microscopy, and Energy-dispersive X-ray analysis was performed. The data were analyzed using One-way ANOVA followed by Holm-Sidak multi-comparison test (p = 0.05). Sealapex showed higher calcium peak than MTA Fillapex, GuttaFlow Bioseal, Adseal and Syntex sealers. MTA Fillapex contained a highest amount of tungstate. Sealapex presented the highest radiopacity value among the tested materials (p < 0.05), whereas MTA Fillapex was the least radiopaque material (p < 0.05). Each root canal sealer contains different compositions of radiopacifiers including bismuth oxide, calcium tungstate and zirconium oxide. The tested root canal sealers had radiopacity values above the ISO-specified limit. Sealapex was the most radiopaque root canal sealer followed by GuttaFlow Bioseal, Syntex, Adseal and MTA Fillapex.

Resumo Os cimentos endodônticos devem conter ótima adesão à dentina radicular, baixa citotoxicidade, radiopacidade suficiente e estabilidade dimensional elevada, que dependem principalmente da sua composição química. Os objetivos deste estudo foram avaliar a composição química de Syntex (Cerkamed, Stalowa Wola, Polônia), Adseal (Meta Biomed, Cheongju-si, Coreia), Sealapex (SybronEndo, Scafati, Itália), MTA Fillapex (Angelus, Londrina, Brasil) e GuttaFlow Bioseal (Coltene/Whaledent, Altstätten, Suíça) e determinar comparativamente a sua radiopacidade. Foram construídos moldes de aço inoxidável com um diâmetro interior de 5 mm e uma profundidade de 2 mm. Os cimentos testados foram misturados e vertidos em moldes. Após a fixação, foram feitas radiografias periapicais digitais dos espécimes (n=12) em condições de exposição padrão e os valores médios de cinza dos espécimes foram medidos utilizando um programa de computação gráfica. Em seguida, as amostras foram examinadas por microscopia eletrônica de varredura, e foi realizada uma análise de raios X dispersiva de energia. Os dados foram analisados utilizando a ANOVA unidirecional seguida do teste de comparação múltipla Holm-Sidak (p = 0,05). O Sealapex mostrou um pico de cálcio mais elevado do que os cimentos MTA Fillapex, GuttaFlow Bioseal, Adseal e Syntex. O MTA Fillapex continha uma quantidade mais elevada de tungstato. O Sealapex apresentou o maior valor de radiopacidade entre os materiais testados (p < 0,05), enquanto que a MTA Fillapex foi o material menos radiopaco (p < 0,05). Cada cimento endodôntico contém diferentes composições de radiopacificadores incluindo óxido de bismuto, tungstato de cálcio e óxido de zircônio. Os cimentos testados apresentaram valores de radiopacidade acima do limite especificado pela ISO. Sealapex foi o cimento obturador mais radiopaco seguido por GuttaFlow Bioseal, Syntex, Adseal e MTA Fillapex.

Radiopacidad de Resinas Acrílicas y Bisacrílicas Usadas como Restauraciones Provisionales

RESUMEN: Una adecuada radiopacidad de los materiales para restauraciones provisorias permite su evaluación en el examen radiográfico. Sin embargo, existe gran desconocimiento sobre el cumplimiento de los requerimientos establecidos por la norma ISO 4049. El objetivo del siguiente estudio fue determinar la radiopacidad de los materiales para provisionalización presentes en el mercado nacional y corroborar si estos cumplen con el valor mínimo requerido por la normativa. Se realizó un estudio experimental in vitro, en el cual se prepararon muestras en forma de discos de 10 mm de diámetro y 1 mm de espesor de resinas acrílicas: Acrílico Autocurable (Marché®), Duralay (Reliance), Caulkâ (Dentsply), ALIKE™ (GC) y resinas bisacrílicas: Protemp™4 (3M, 2008), LuxatempStar (DMG), Luxacrown (DMG), Structur Premium (VOCO), ExperTemp™ (Ultradent) y Acrytemp (Zhermack). Las muestras fueron radiografiadas junto a una cuña de aluminio escalonada. Las imágenes fueron analizadas para determinar el valor en escala de grises y su respectivo valor en mm de aluminio. Los datos fueron analizados para verificar si cumplen con la normativa ISO. Se encontraron diferencias estadísticamente significativas. La radiopacidad equivalente de las resinas acrílicas en mm de Al en orden descendente fue de 0,85 ± 0,08 para ALIKE™, 0,72 ± 0,32 para acrílico Marché®, 0,65 ± 0,25 para Caulkâ y 0,56 ± 0,05 para Duralay, siendo todos menores a lo requerido por la norma. La radiopacidad equivalente de las resinas bisacrílicas fue de 1,75 ± 0,2 para Acrytemp, 1,51± 0,27 para Luxacrown, 1,47 ± 0,14 para Structur Premium, 1,43 ± 0,23 para LuxatempStar, 1,02 ± 0,28 para Protemp™4 y 1± 0,1 para ExperTemp™, los cuales son mayores a lo exigido por la norma. En conclusión, las resinas bisacrílicasevaluadas en este estudio cumplen con el requisito de radiopacidad exigido, a diferencia de las acrílicas que no lo cumplen.

ABSTRACT: An adequate radiopacity of materials for provisionalization allows its proper evaluation on the radiographicexam. However, there is a lack of knowledge about compliance with the requirements established by the ISO 4049 norm. The aim of this study was to determine the radiopacity of provisionalization materials available in the national market and verify if they comply with the minimum requirements of ISO regulations. An in vitro experimental study was carried out, samples of 10 mm in diameter and 1 mm thickness of acrylic resins: Self-Cure Acrylic (Marché®), Duralay (Reliance), Caulkâ (Dentsply), Alike™ (GC) and by sacrilic resins: Protemp™4 (3M), Luxatemp Star (DMG), Luxacrown (DMG), Structur Premium (VOCO), ExperTemp™ (Ultradent), Acrytemp (Zhermack) were prepared. The samples were x-rayed together with a stepped aluminum wedge. The images were analyzed to determine the gray scale value and its equivalent value in mm of Aluminum. The data was analyzed to verify compliance with the ISO standard. Statistically significant differences were found. The equivalent radiopacity of acrylicresins in mm of Al in descending order was 0.85± 0.08 for ALIKE™, 0.72 ± 0.32 for acrylic Marché®, 0.65 ± 0.25 forCaulkâ and 0.56 ± 0.05 forDuralay, all being less than the required by norm. The equivalent radiopacity of by sacrilic resins was 1.75 ± 0.2 for Acrytemp, 1.51± 0.27 for Luxacrown, 1.47 ± 0.14 for Structur Premium, 1.43 ± 0.23 for LuxatempStar, 1.02 ± 0.28 forProtemp™4 and 1± 0.1 forExperTemp™,which are greater than the requirements. In conclusion, the bisacrylic resins evaluated in this study comply with the radiopacity standard, however the acrylic resins evaluated do not comply.

Radiopacidad de Materiales Utilizados Como Sustituto Dentinario / Radiopacity of Materials Used as Dentin Substitutes

El objetivo de este estudio fue comparar la radiopacidad de distintos materiales utilizados como sustitutos de la dentina según norma ISO 6876. Se utilizaron Biodentine-Septodont (a base de silicato de calcio), Equia Forte ­ GC Corporation (ionómero vítreo convencional), Sure Fill SDR Flow ­ Dentsply Sirona (composite bulk-fill), MTA Densell Reparative - Densell (a base de silicato de calcio). Se confeccionaron 12 probetas cilíndricas, tres por cada material, siguiendo las instrucciones de los respectivos fabricantes y se colocaron en estufa a 37°C durante su fraguado. Se tomaron radiografías oclusales digitales junto a una cuña de aluminio graduada según norma ISO 6876. En cada imagen se determinaron los valores de L de la escala CieLab (negro-blanco) con el programa Photoshop (Adobe). Los resultados se analizaron estadísticamente mediante ANOVA y prueba de Tukey (AU)

Physicochemical properties of two epoxy resin-based sealants: Topseal® and AdSeal™. A comparative study / Propiedades físico-químicas de dos selladores a base de resina epóxica: Topseal® y AdSeal™. Estudio comparativo

Abstract Introduction: a new epoxy resin-based root-canal sealer (AdSeal™) recently appeared on the market. The aim of this study was to evaluate the radiopacity, flow rate, and film thickness of this sealant compared to Topseal®. Methods: the tests were conducted in compliance with ISO 6876:2012 standards. To evaluate radiopacity, 5 discs of each sealant measuring 10 mm in diameter by 1 mm thick were crafted, comparing their radiographic density in mm of aluminum (Al). For flow rate analysis, 0.05 ml of sealant were placed between 2 glass plates under a weight of 120 g for 10 minutes. The diameters of the formed discs were measured with a calibrator and analyzed with the imageJ software. For film thickness analysis, the sealants were placed between 2 glass plates, applying a load of 150N with a universal testing machine (AGIS 5KN) for 10 minutes. Distance between the glass plates was measured using a stereomicroscope at three equidistant points. Results: Topseal® showed more radiopacity (Wilcoxon p < 0.05) and less flow rate than AdSeal™, with statistically significant differences (Anova p = 0.0001863). The film thickness values are above the limit allowed by standard 6876, possibly because of the methodology used in this study; however, no statistically significant difference was found between the sealants (Anova p = 0.4927). Conclusions: the radiopacity and flow rate of AdSeal™ and Topseal® sealants comply with the ISO 6876:2012 standard, but the film thickness values fail to meet the standard.

Resumen Introducción: un nuevo sellador de conductos radiculares a base de resina epóxica (AdSeal™) apareció recientemente en el mercado. El objetivo de este estudio consistió en evaluar la radiopacidad, fluidez y espesor de película de este sellador comparado con el Topseal®. Métodos: las pruebas fueron realizadas en concordancia con la norma ISO 6876:2012. Para evaluar la radiopacidad se elaboraron 5 discos de cada sellador de 10 mm de diámetro por 1 mm de espesor, comparando su densidad radiográfica en mm de aluminio (Al). Para el análisis de fluidez se colocaron 0,05 ml de sellador entre 2 placas de vidrio bajo un peso de 120 g por 10 minutos; los diámetros de los discos formados se midieron con un calibrador y fueron analizados con el software imageJ. Para el análisis de espesor de película los selladores se colocaron entre 2 placas de vidrio, se aplicó una carga de 150 N con una máquina universal de ensayos (AGIS 5KN) por 10 minutos, y la distancia entre las placas de vidrio fue medida con ayuda de un estereomicroscopio en tres puntos equidistantes. Resultados: el Topseal® tuvo mayor radiopacidad (Wilcoxon p < 0,05) y menor fluidez que el AdSeal™ con diferencias estadísticamente significativas (Anova p = 0,0001863). Los valores de espesor de película están por encima del límite permitido por la norma 6876, posiblemente por la metodología utilizada en el estudio; sin embargo, no se encontró diferencia estadísticamente significativa entre los selladores (Anova p = 0,4927). Conclusiones: la radiopacidad y fluidez de los selladores AdSeal™ y Topseal® cumplen con la Norma ISO 6876:2012, pero los valores de espesor de película no cumplen con la norma.

Radiopacidad de Cementos de Resina Compuesta Evaluados con Técnica Radiográfica Digital / "Radiopacity of Resin Cements Evaluated with Digital Radiographic Technique"

RESUMEN: Objetivo: comparar la radiopacidad de distintos cementos de resina y corroborar si cumplen con los requisitos de normativas ISO. Material y método: Se prepararon muestras de 1 mm de grosor de los cementos de resina: RelyX U200 (3M ESPE), Calibra (Dentsply Sirona), Calibra Universal (Dentsply Sirona) y Bifix SE (VOCO). Las muestras fueron radiografiadas junto a una cuña de aluminio escalonada. Las imágenes fueron analizadas para determinar el valor en escala de grises y su respectivo valor en mm de Al. Los datos fueron analizados para comparar la radiopacidad de los materiales entre sí y con los requisitos establecidos por normas ISO. Resultados: La radiopacidad equivalente en mm de Al en orden descendiente fue de 2,84 ± 0,18 para Calibra, 2,37 ± 0,15 para Bifix SE, 2,26 ± 0,14 para Calibra Universal y de 1,67 ± 0,07 para RelyX U200. Estos valores son todos mayores al mismo grosor de aluminio exigido por la norma ISO 4049. Se establecieron diferencias estadísticamente significativas entre los cementos. Conclusiones: Se determinó que existen diferencias en la radiopacidad entre los cementos de resina compuesta estudiados. Sin embargo, todos los cementos evaluados cumplen con la norma ISO-4049 de radiopacidad.

ABSTRACT: Objective: Compare the radiopacity of different resin cements and verify their compliance with the requirements of ISO regulations. Material and method: Samples -10 mm in diameter and 1 mm thickness- of the resin cements RelyX U200 (3M ESPE), Calibra (Dentsply Sirona), Universal Calibra (Dentsply Sirona) and Bifix SE (VOCO) were prepared. Radiographies of the samples with a stepped aluminum wedge were obtained. For each sample, the grayscale and mm of Al values were calculated. The data were analyzed to compare the radiopacity of the materials and to contrast them with the requirements established by ISO standards. Results: The equivalent radiopacity in mm of Al in descending order was 2.84 ± 0.18 for Calibra, 2.37 ± 0.15 for Bifix SE, 2.26 ± 0.14 for Calibra Universal and 1.67 ± 0.07 for RelyX U200. These values exceed the value required by ISO 4049 standard. Statistically significant differences were established between the cements. Conclusion: There are differences in the radiopacity of the resin cements studied. However, all the cements complied with ISO 4049 radiopacity standards.

Radiopacidade de dentes artificiais para treinamento pré-clínico de endodontia / Artificial tooth radiopacity for preclinical endodontic training

Resumo Introdução Dentes artificiais têm sido utilizados para a prática odontológica e, segundo seus fabricantes, apresentam muita similaridade aos dentes humanos para treinamento. Objetivo Avaliar a radiopacidade de dentes endodônticos artificiais para uso em atividades de ensino e saber a percepção de docentes quanto à análise radiográfica. Material e método Trinta réplicas de incisivos centrais superiores de três marcas comerciais (Fábrica de Sorrisos, IM do Brasil e Real Dent) e um incisivo humano foram utilizados. Foram dispostos sobre um sensor radiográfico o dente humano e um dente artificial de cada empresa. As análises de radiopacidade foram feitas no programa Photoshop® em triplicata em quatro regiões distintas: porção central da coroa e nos terços cervical, médio e apical do canal. A percepção quanto à utilização dos dentes como instrumento prático de ensino foi avaliada por meio de um questionário aplicado a oito professores de endodontia. Para análise estatística dos valores de radiopacidade, foi utilizada a ANOVA, seguida do teste de Tukey. Foi empregado um nível de significância de 5%. Para análise do questionário, foram empregados métodos descritivos e por porcentagem de dados no que se refere à frequência das respostas. Resultado Houve diferença de radiopacidade entre os diferentes dentes testados em cada região analisada (p > 0,05). Na percepção dos professores com relação à utilização dos dentes no ensino, eles colocaram em ordem crescente os seguintes dentes para uso: IM do Brasil, Fábrica de Sorrisos, Real Dent e humano. Conclusão A radiopacidade dos dentes artificiais foi diferente do humano. O dente artificial da Fábrica de Sorrisos apresentou os maiores valores de radiopacidade. Contudo, os professores consideraram ideais para utilização no ensino apenas o dente humano e o dente da Real Dent.

Abstract Introduction Artificial teeth have been used for dental practice which, acoording to their manufactures, bear much similarity to human teeth for training. Objective To evaluate radiopacity of artificial endodontic teeth for use in teaching activities and to know the perception of teachers regarding radiographic analysis. Material and method Thirty replicates of upper central incisors of three trade marks (Fábrica de Sorrisos, IM do Brasil and Real Dent) and a human incisor were used. On a radiographic sensor, human tooth and one artificial tooth of each marks were arranged. Radiopacity analyzes were performed using Photoshop® in triplicate in four distinct regions: central portion of the crown and in the cervical, middle and apical thirds of the canal. The perception about the use of teeth as a practical teaching instrument was evaluated through a questionnaire applied to eight teachers of Endodontics. For statistical analysis of the radiopacity values ​​ANOVA was used, followed by the Tukey test. Significance level of 5%. For the analysis of the questionnaire were used descriptive methods and percentage of data regarding the frequency of responses. Result There was a difference in radiopacity between the different teeth tested, in each region analyzed (P > 0.05). In the teachers' perception regarding the use of teeth in teaching, the teachers placed the following teeth for use: IM do Brasil, Fábrica de Sorrisos, Real Dent and human. Conclusion The radiopacity of the artificial teeth was different from the human teeth. The artificial tooth of the Fábrica de Sorrisos presented the highest values ​​of radiopacity. The teachers considered ideal for use in teaching only the human teeth and the prototype Real Dent.

Discoloration and radiopacity of white mineral trioxide aggregate with various radiopacifiers / 대한치과재료학회지

The use of the mineral trioxide aggregate (MTA) has been expanded as the material can be applied on various treatment of endodontic care, which also has many advantages including bioactivity. Still, the discolorations of the materials have been presented as a concern related to esthetic appearances, which is caused by the presence of radiopacifiers. Therefore, the aim of this study was to investigate the color stability and radiopacity of white MTA with various radiopacifiers. Four different radiopacifiers [bismuth oxide (BM), calcium tungstate (CT), barium oxide (BO), and zirconium oxide (ZO)] were used. The radiopacity was tested according to ISO 6876, and the color change before and after immersing in a 5% hypochlorite solution was tested using a spectrophotometer. The group with no radiopacifier (NR) was used as a negative control and ProRoot MTA (PR) was used as the commercial control. The immersion of the PR and BM in sodium hypochlorite resulted in a dark brown discoloration, in which the values were higher than the rest of the group (p0.05). In terms of the radiopacity, the NR showed the lowest value as expected (p<0.05). Meanwhile, the BM showed the highest value (p<0.05), followed by PR and BO (p<0.05). The NR showed the lowest radiopacity values. The result of this study will be useful for future development of MTA that would have clinically adequate radiopacity with minimum discoloration.

In vitro analysis of dental ceramics: evaluation of the radiopacity and chemical composition by Raman spectroscopy / Análise in vitro de cerâmicas odontológicas: avaliação da radiopacidade e composição química por espectroscopia Raman

Objective: This study compared the radiopacity of different ceramic systems by means of digital radiographs and evaluate the chemical composition of the samples by Raman spectroscopy. The hypothesis tested was that there was a difference in radiopacity among the tested materials. Material and Methods: Specimens were prepared for each ceramic tested: FLD - VM7 (VITA Zahnfabrik), LD - IPS Empress e.max Press (IPS Empress), AL - In Ceram Alumina (VITA Zahnfabrik), ALYZ - In Ceram Zirconia (VITA Zahnfabrik), YZ - Lava All Ceram (3M/ESPE), and MYZ - Zirconzahn (Talladium Brazil). The specimens were radiographed and submitted to radiographic density readings using a histogram tool. The spectrometer coupled to a petrographic microscope was used for Raman spectroscopy measurements. Analysis of variance (ANOVA) and a Tukey post-hoc test were used to compare radiopacity of the different materials. Results: For all tested materials, the radiopacity showed statistically significant differences, except YZ and MYZ. Lava All Ceram and ZirkonZahn had high radiopacity values and VM7 and IPS Empress e.max Press showed lower radiopacity than human dental structures. Conclusion: It was possible to conclude that radiopacity is closely linked to ceramic chemical composition. (AU)

Objetivo: Este estudo comparou a radiopacidade de diferentes sistemas cerâmicos por meio de radiografias digitais e avaliou a composição química das amostras por espectroscopia Raman. A hipótese testada foi que haveria diferença na radiopacidade entre os materiais testados. Material e Métodos: Os espécimes foram preparados para cada cerâmica testada: FLD - VM7 (VITA Zahnfabrik), LD - Impressora IPS Empress e.max (IPS Empress), AL - Em Ceram Alumina (VITA Zahnfabrik), ALYZ - In Ceram Zirconia (VITA Zahnfabrik), YZ - Lava All Ceram (3M / ESPE) e MYZ - Zirconzahn (Talladium Brasil). Os espécimes foram radiografados e submetidos a leituras de densidade radiográfica utilizando uma ferramenta de histograma. O espectrômetro acoplado a um microscópio petrográfico foi utilizado para medidas de espectroscopia Raman. Análise de variância (ANOVA) e teste post-hoc de Tukey foram usados para comparar a radiopacidade dos diferentes materiais. Resultados: Para todos os materiais testados, a radiopacidade apresentou diferenças estatisticamente significantes, exceto YZ e MYZ. Lava All Ceram e ZirkonZahn apresentaram altos valores de radiopacidade e o VM7 e o IPS Empress e.max Press apresentaram menor radiopacidade do que as estruturas dentais humanas. Conclusão: Foi possível concluir que a radiopacidade está intimamente ligada à composição química da cerâmica. (AU)

Radiopacity Evaluation of Gutta-Percha Points in Thinner Samples than the ANSI/ADA Recommendation

Abstract The aim of this study was to evaluate the radiopacity of different gutta-percha points (Endo Points®, Dentsply®, Tanari®, Meta®, Roeko® and Odous®) in samples of 1 mm thick as established by ANSI/ADA Specification #57 and ISO 6876/2001, in comparison with thinner samples. Twelve test specimens for each material, four for each thickness (0.3, 0.6, and 1 mm and diameter of 8 mm), were laminated and compressed between two polished glass plates until the desirable thickness. Digital radiographs were obtained along with a graduated aluminum stepwedge varying from 1 to 10 mm in thickness. The X-ray unit was set at 70 kVp, 10 mA and 0.4 s exposure time, at a focal distance of 36 cm. One calibrated observer quantified the average values of pixels with Adobe Photoshop® software. Data were analyzed using ANOVA and Tukey tests, at 5% significance level. At 0.6 and 1 mm thickness, all the tested materials showed radiopacity higher than 3 mm of aluminum (reference value). At 0.3 mm thickness, Odous and Tanari presented significantly less radiopacity than the reference, and the other materials showed similar radiopacity to the reference. The study concluded that the materials demonstrated different radiopacities and all had values above the minimum recommended by ANSI/ADA specification #57, being Odous and Tanari less radiopaque than the reference value in thinner samples (0.3mm).

Resumo O objetivo deste estudo foi avaliar a radipacidade de diferentes pontas de guta-percha (Endo Points®, Dentsply®, Tanari®, Meta®, Roeko® e Odous®) em amostras de 1 mm de espessura, conforme estabelecido pela especificação #57 da ANSI/ADA e pela ISO 6876/2001, em comparação com amostras de menor espessura. Doze amostras de cada material, quatro para cada espessura (0,3, 0,6 e 1 mm; 8 mm de diâmetro), foram confeccionadas por meio de laminação e compressão entre duas lâminas de vidro polidas, até a espessura desejada. Radiografias digitais foram obtidas juntamente com uma escala de alumínio graduada, com espessuras variando de 1 a 10 mm. O aparelho de raios X foi ajustado para 70 kVp, 10 mA, 0,4s de tempo de exposição, com distância focal de 36 cm. Um observador calibrado quantificou a média dos valores de pixel no programa Adobe Photoshop®. Os dados foram analisados utilizando os testes ANOVA e Tukey, com nível de significância de 5%. Nas espessuras de 0,6 e 1 mm, todos os materiais testados apresentaram radiopacidade maior do que 3 mm de alumínio (valor de referência). Na espessura de 0,3 mm, Odous e Tanari apresentaram radiopacidade significativamente menor que a referência, e as outras marcas mostraram radiopacidade semelhante à referência. Conclui-se que os materiais apresentaram diferentes radiopacidades e todos mostraram valores acima do mínimo recomendado pela especificação #57 da ANSI/ADA, sendo Odous e Tanari menos radiopacos do que o valor de referência nas amostras mais finas (0.3 mm).

Physical properties of a new resin-based root canal sealer in comparison with AH Plus Jet

PURPOSE: The aim of this study was to assess the physical properties of a novel resin-based endodontic sealer, Any-Seal, in comparison with AH Plus Jet. MATERIALS AND METHODS: Flow, radiopacity and compressive strength were examined according to ISO 6876/2001. For flow test, 0.05 mL of sealer was placed between glass plate and 100 g weight were applied. Ten minutes after mixing the sealers, the load was removed and the diameters of the compressed sealer discs were measured. For radiopacity, 10 mm diameter and 1 mm thickness sample were fabricated and took radiograph with an aluminum step-wedge and analyzed using imaging program. For compressive strength test, 4 mm × 6 mm cylindrical specimen was fabricated and tested after 24 hours and 1 week using Universal testing machine. RESULTS: Both tested sealers were consistent with ISO 6876/2001 in the flow and radiopacity test. The flow values of both sealers were not significantly different (P > 0.05). AH Plus Jet had significantly higher radiopacity (P < 0.05). AH Plus Jet showed higher compressive strength at both time intervals (P < 0.05). CONCLUSION: Any-Seal showed low compressive strength until after 1 week, so its physical and biological aspect should be evaluated more before clinical use.

Physicochemical Properties of Root Canal Filling Materials for Primary Teeth

Abstract This study evaluated physiochemical proprieties of a calcium hydroxide-based paste (Calen(r)) combined with a zinc oxide cement at different ratios (1:0.5, 1:0.65, 1:0.8 and 1:1). Materials were compared regarding setting time, pH variation, radiopacity, solubility, dimensional changes, flow and release of chemical elements. Data were analyzed statistically by ANOVA and Tukey's test (α=0.05). Longer setting time and higher dimensional changes and solubility values were exhibited by 1:0.65 and 1:0.5 ratios (p<0.05). The 1:0.5 and 1:0.65 ratios exhibited the highest pH values at all time points. All materials exhibited high radiopacity values. Significant differences were found only between 1:0.5 and 1:1 ratios for calcium and zinc release (p<0.05), whereas the amount of zirconium was similar among all groups (p>0.05). Considering the evaluated proprieties, combinations of Calen(r) paste with ZO at 1:0.5 and 1:0.65 ratios had the best results as root canal filling materials for use in primary teeth.

Resumo O objetivo do presente estudo foi avaliar propriedades físico-químicas da pasta à base de hidróxido de cálcio (Calen(r)) combinado com diferentes proporções de óxido de zinco (OZ) (1:0,5 e 1:0,65, 1:0,8 e 1:1) (Calen(r) /OZ). Os materiais foram comparados quanto ao tempo de endurecimento, variação do pH, radiopacidade, solubilidade, alterações dimensionais, escoamento e liberação de elementos químicos. Os dados obtidos foram submetidos à análise de variância (nível de 5% de significância). Maior grau de endurecimento, valores de alterações dimensionais, e solubilidade foram encontrados para Calen(r) /OZ 1:0,65 e 1:0,5. Calen(r) /OZ 1:0,5 e 1:0,65, apresentaram os maiores valores de pH em todos os momentos. Todos os materiais apresentaram valores elevados de radiopacidade com diferenças significativas (p>.05). Foram encontradas diferenças significativas apenas entre Calen(r) /OZ de 1:0,5 e 1:1 na liberação de cálcio e zinco (p< 0,05), enquanto que a quantidade de zircônia foi semelhante entre todos os grupos analisados (p>.05). Em relação às propriedades avaliadas no presente estudo, as combinações de Calen(r) com óxido de zinco nas proporções 1:0,5 e 1:0,65 são mais adequadas como material obturador para os canais radiculares de dentes decíduos.

Comparative study of the radiopacity of resin cements used in aesthetic dentistry

PURPOSE: The aim of this study was to compare the radiopacity of 6 modern resin cements with that of human enamel and dentine using the Digora digital radiography system, to verify whether they meet the requirements of ANSI/ADA specification no. 27/1993 and the ISO 4049/2000 standard and assess whether their radiopacity is influenced by the thickness of the cement employed. MATERIALS AND METHODS: Three 3-thickness samples (0.5, 1 and 1.5 mm) were fabricated for each material. The individual cement samples were radiographed on the CCD sensor next to the aluminium wedge and the tooth samples. Five radiographs were made of each sample and therefore five readings of radiographic density were taken for each thickness of the materials. The radiopacity was measured in pixels using Digora 2.6 software. The calibration curve obtained from the mean values of each step of the wedge made it possible to obtain the equivalent in mm of aluminium for each mm of the luting material. RESULTS: With the exception of Variolink Veneer Medium Value 0, all the cements studied were more radiopaque than enamel and dentin (P<.05) and complied with the ISO and ANSI/ADA requirements (P<.001). The radiopacity of all the cements examined depended on their thickness: the thicker the material, the greater its radiopacity. CONCLUSION: All materials except Variolink Veneer Medium Value 0 yielded radiopacity values that complied with the recommendations of the ISO and ANSI/ADA. Variolink Veneer Medium Value 0 showed less radiopacity than enamel and dentin.

Physicochemical Properties and Interfacial Adaptation of Root Canal Sealers

This study compared the physicochemical properties and interfacial adaptation to canal walls of Endo-CPM-Sealer, Sealapex and Activ GP with the well-established AH Plus sealer. The following analyses were performed: radiopacity, pH variation and solubility using samples of each material and scanning electron microscopy of root-filled bovine incisors to evaluate the interfacial adaptation. Data were analyzed by the parametric and no-parametric tests (α=0.05). All materials were in accordance with the ANSI/ADA requirements for radiopacity. Endo-CPM-Sealer presented the lowest radiopacity values and AH Plus was the most radiopaque sealer (p=0.0001). Except for ActiV GP, which was acidic, all other sealers had basic chemical nature and released hydroxyl ions. Regarding solubility, all materials met the ANSI/ADA recommendations, with no statistically significant difference between the sealers (p=0.0834). AH Plus presented the best adaptation to canal walls in the middle (p=0.0023) and apical (p=0.0012) thirds, while the sealers Activ GP and Endo-CPM-Sealer had poor adaptation to the canal walls. All sealers, except for ActiV GP, were alkaline and all of them fulfilled the ANSI/ADA requirements for radiopacity and solubility. Regarding the interfacial adaptation, AH Plus was superior to the others considering the adaptation to the bovine root canal walls.

Este estudo comparou as propriedades físico-químicas e a adaptação interfacial às paredes do canal dos cimentos Endo-CPM-Sealer, Sealapex e Activ GP com o bem estabelecido cimento AH Plus. As seguintes análises foram realizadas: radiopacidade, variação de pH e de solubilidade utilizando amostras de cada material, e microscopia eletrônica de varredura utilizando incisivos bovinos obturados para avaliar a adaptação interfacial. Os dados foram analisados utilizando testes paramétricos e não-paramétricos (α=0,05). Todos os materiais estavam de acordo com os requerimentos da ANSI/ADA para radiopacidade, sendo que o Endo-CPM-Sealer apresentou os menores valores de radiopacidade e o AH Plus foi o cimento mais radiopaco (p=0,0001). Exceto o Activ GP, que foi ácido, todos os outros cimentos apresentaram natureza química básica e liberaram íons hidroxila. Com relação à solubilidade, todos os materiais estavam de acordo com as recomendações da ANSI /ADA, sem diferença significante entre os cimentos (p=0,0834). O AH Plus apresentou a melhor adaptação às paredes do canal nos terços médio (p=0,0023) e apical (p=0,0012), enquanto que os cimentos Activ GP e Endo-CPM-Sealer apresentaram uma pobre adaptação às paredes do canal. Em conclusão, todos os cimentos, exceto o Activ GP, foram alcalinos e todos preencheram os requerimentos da ANSI/ADA para radiopacidade e solubilidade. Com relação à adaptação interfacial, o AH Plus foi superior aos demais para adaptação às paredes do canal radicular de incisivos bovinos.

Comparative study on the radiopacity of different resin-based implant cements / 대한치과보철학회지

PURPOSE: This study was aimed to compare the radiopacity of four kinds of currently available resin based implant cements using digital radiography. MATERIALS AND METHODS: Four resin-based implant cements ((Estemp Implant(TM) (Spident, Incheon, Korea), Premier(R) Implant (Premier, Pennsylvania, USA), Cem-Implant(TM) (B.J.M lab, Or-yehuda, Israel), InterCem(TM) (SCI-PHARM, California, USA)) and control group (Elite Cement 100(TM) (GC, Tokyo, Japan)) were mixed and cured according to the manufacturer's instructions on the custom made split-type metal mold. A total of 150 specimens of each cement were prepared and each specimen (purity over 99%) was placed side-by-side with an aluminum step wedge for image taking with Intraoral X-ray unit (Esx, Vatech, Korea) and digital X-ray sensor (EzSensor, Vatech, Korea). For the evaluation of aluminum wedge equivalent thickness (mm Al), Image J 1.47 m (Wayne Rasband, National Institutes of Health, USA) and Color inspector 3D ver 2.0 (Interaktive Visualisierung von Farbraumen, Berlin, Germany) programs were used. RESULT: Among the 5 cements, Elite cement 100(TM) (control group) showed the highest radio-opacity in all thickness. In the experimental group, InterCem(TM) had the highest radio-opacity followed by Premier(R) Implant Cement(TM), Cem-Implant(TM) and Estemp Implant(TM). In addition, InterCem(TM) showed radio-opacity that met the ISO No. 4049 standard in all the tested specimen thickness. Cem-Implant on 0.5 mm thickness showed radiopacity that met the ISO No. 4049 standard. CONCLUSION: Among the implant resin-based cements tested in the study, Premier(R) Implant Cement and Estemp Implant(TM) did not show appropriate radio-opacity. Only InterCem(TM) and Cem-Implant(TM) 0.5 mm specimen had the proper radiopacity and met the experiment standard.

Avaliação da radiopacidade de diferentes materiais utilizados como retrobturadores / Evaluation of radiopacity of different used as root-end filling materials

Objetivo: O presente estudo tem como objetivo avaliar a radiopacidade de três materiais utilizados como retrobturadores. Métodos: Foram avaliados a radiopacidade de três cimentos: Sealer 26, Cimento Portland e Fillapex associado com 50% de cimento Portland.Para a determinação da radiopacidade, foram confeccionados corpos de provas cilíndricos de 10 mm de diâmetro e 1 mm de altura com os cimentos em teste e cilindros de dentina de mesma espessura, de acordo com a norma ISO 6876:2001. Após a sensibilização e processamento das películas, as imagens foram digitalizadas e analisadas quanto a densidade radiográfica no programa Digora 1.51. O valor da radiopacidade foi determinado em densidade radiográfica que foi, também, convertida em milímetros de alumínio (mm Al). Resultados: Os resultados demonstraram que o Sealer 26 possui maior radiopacidade, seguido pelo Fillapex associado com 50% de Cimento Portland e o cimento Portland. Conclusão: Conclui-se que todos os materiais apresentaram radiopacidade maior que a dentina e as normas da ISO, com exceção do cimento Portland.

Aim: The present study aims to evaluate the radiopacity of three used as root-end filling materials. Methods: To evaluated the radiopacity of three cement: Sealer 26, Fillapex associated with 50% of Portland cement and Portland cement. For the determination of radiopacity, cylindrical specimens with 10 mm in diameter and 1mm in thickness were made with the cements under test and dentin cylinders of equal thickness, according to ISO 6876:2001. After the raising and processing of films, the images were digitized andanalyzed for the radiographic density in Digora 1.51. The value of radiopacity was determined in radiographic density that was also converted into millimetres of aluminium (mm Al). Results: The results showed that the Sealer 26 has greater radiopacity, followed by Fillapex associated with 50% of Portland cement and Portland cement. Conclusion: It is concluded that all materials presented radiopacity is greater than the dentin and the ISO standards, with the exception of Portland cement.